Multi-layered perovskites, devices, and methods of making the same

ABSTRACT

Methods are described that include contacting an alkyl ammonium metal halide film with an alkyl ammonium halide, where the alkyl ammonium metal halide film includes a first halogen and a metal, the alkyl ammonium halide includes a second halogen, such that the contacting forms an alkyl ammonium metal mixed-halide film that interfaces with the alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film includes the first halogen, the second halogen, and the metal.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefits of U.S. Provisional Application Nos. 62/258,201 and 62/303,449 filed Nov. 20, 2015 and Mar. 4, 2016 respectively, the contents of which are incorporated herein by reference in their entirety.

CONTRACTUAL ORIGIN

The United States Government has rights in this invention under Contract No. DE-AC36-08GO28308 between the United States Department of Energy and the Alliance for Sustainable Energy, LLC, the Manager and Operator of the National Renewable Energy Laboratory.

BACKGROUND

Perovskite halides (e.g., CH₃NH₃PbI₃ or MAPbI₃) represent a new class of light absorbers that have demonstrated exceptional, unparalleled progress in solar cell performance from 3.8% in 2009 to a certified 17.9% in 2014. Since then, perovskites have attracted increasing worldwide attention for a variety of optoelectronic fields, including solar cells, light-emitting diodes, and laser applications. However, the standard perovskite MAPbI₃ is found to have potential stability issues in moisture-containing environments, especially at elevated temperatures with exposure to light. Thus, improved perovskite halide films are needed for these materials to provide technically and economically viable solar cell alternatives to the current incumbent technologies such as silicon solar cells.

SUMMARY

An aspect of the present disclosure is a method that includes contacting an alkyl ammonium metal halide film with an alkyl ammonium halide, where the alkyl ammonium metal halide film includes a first halogen and a metal, the alkyl ammonium halide includes a second halogen, such that the contacting forms an alkyl ammonium metal mixed-halide film that interfaces with the alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film includes the first halogen, the second halogen, and the metal. In some embodiments of the present disclosure, during the contacting, the alkyl ammonium halide may be in at least one of a liquid phase and/or a vapor phase. In some embodiments of the present disclosure, the contacting may be in the liquid phase, and the liquid phase may be in a solution with a solvent. In some embodiments of the present disclosure, the metal may include at least one of lead, tin, and/or germanium.

In some embodiments of the present disclosure, the alkyl ammonium metal halide film may include CH₃NH₃PbI₃, the first halogen may include iodine, and the metal may include lead. In some embodiments of the present disclosure, the alkyl ammonium halide may include CH₃NH₃Br (MABr), and the second halogen may include bromine. In some embodiments of the present disclosure, the alkyl ammonium metal halide film may be substantially insoluble in the solvent, and the alkyl ammonium halide may be substantially soluble in the solvent. In some embodiments of the present disclosure, the solvent may include at least one of isopropanol and/or tert-butanol. In some embodiments of the present disclosure, the alkyl ammonium metal mixed-halide film may include CH₃NH₃PbI_(3-x)Br_(x), the first halogen may include iodine, the second halogen may include bromine, the metal may include lead, and x may be between greater than 0 and about 3.

In some embodiments of the present disclosure, the alkyl ammonium metal mixed-halide film may have a thickness between about 1 nanometer and about 1000 nanometers. In some embodiments of the present disclosure, the thickness may be between about 3 nanometers and about 300 nanometers. In some embodiments of the present disclosure, the method may further include heating the alkyl ammonium metal halide film and the alkyl ammonium metal mixed-halide film. In some embodiments of the present disclosure, the heating may include attaining an average bulk temperature for the alkyl ammonium metal halide film and the alkyl ammonium metal mixed-halide film between about 50° C. and about 300° C. In some embodiments of the present disclosure, the average bulk temperature may be between about 100° C. and about 150° C. In some embodiments of the present disclosure, the method may further include, before the contacting, depositing the alkyl ammonium metal halide film onto a substrate. In some embodiments of the present disclosure, the MABr may be in the solution at a concentration between greater than 0 mg MABr/ml to about 8 mg MABr/ml. In some embodiments of the present disclosure, the concentration may be between greater than 0 mg MABr/ml to about 2 mg MABr/ml.

An aspect of the present disclosure is a device that includes, in order, an alkyl ammonium metal halide film that includes a first halogen, and an alkyl ammonium metal mixed-halide film that includes the first halogen and a second halogen, where the alkyl ammonium metal halide film has a thickness of about 1 nanometer to about 1000 nanometers, and a thickness of the alkyl ammonium metal mixed-halide film is less than or equal to the thickness of the alkyl ammonium metal halide film. In some embodiments of the present disclosure, the thickness of the alkyl ammonium metal mixed-halide film may be between about 1 nanometer to about 1000 nanometers. In some embodiments of the present disclosure, the metal may include at least one of lead, tin, or germanium. In some embodiments of the present disclosure, the alkyl ammonium metal halide film may include CH₃NH₃PbI₃, the first halogen may include iodine, and the metal may include lead. In some embodiments of the present disclosure, the alkyl ammonium lead mixed-halide film may include CH₃NH₃PbT_(3-x)Br_(x), the first halogen may include iodine, the second halogen may include bromine, the metal may include lead, and x may be between greater than 0 and about 3.

BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments are illustrated in referenced figures of the drawings. It is intended that the embodiments and figures disclosed herein are to be considered illustrative rather than limiting.

FIG. 1 illustrates a schematic of a perovskite material, according to some embodiments of the present disclosure.

FIG. 2 illustrates a method of making a perovskite device, according to some embodiments of the present disclosure.

FIGS. 3A and 3B illustrate a perovskite device having two perovskite films, according to some embodiments of the present disclosure.

FIGS. 4A and 4B illustrate scanning electron microscopy (SEM) images of the top view of a (FIG. 4A) standard MAPbI₃ film and (FIG. 4B) MABr treated MAPbI₃ film made by methods according to some embodiments of the present disclosure.

FIG. 5 illustrates ultraviolet-visible (UV-vis) absorption spectra of MAPbI₃ films with and without MABr treatment made by methods according to some embodiments of the present disclosure.

FIG. 6 illustrates X-ray diffraction patterns of MAPbI₃ films with and without MABr treatment made by methods according to some embodiments of the present disclosure.

FIGS. 7A and 7B illustrate the impact of MABr treatment on the photoluminescence (PL) properties of a starting MAPbI₃ thin film, according to some embodiments of the present disclosure: (FIG. 7a ) steady-state PL and (FIG. 7b ) time-resolved PL spectra of MAPbI₃ films with and without MABr treatment.

FIG. 8 illustrates X-ray photoelectron spectroscopy (XPS) measurements of core level analysis of MAPbI₃ with and without MABr treatment, according to some embodiments of the present disclosure.

FIG. 9 illustrates photocurrent density-voltage (J-V) curves of perovskite solar cells based on films of MAPbI₃ with and without MABr treatment, according to some embodiments of the present disclosure.

FIG. 10 illustrates external quantum efficiency (EQE) spectra of solar cells based on MAPbI₃ and MABr-treated perovskite films made by methods according to some embodiments of the present disclosure.

FIGS. 11A-D illustrate photos of as-prepared (FIG. 11A) and aged (FIG. 11C) MAPbI₃ film and as-prepared (FIG. 11B) and aged (FIG. 11D) MABr-treated MAPbI₃ film made by methods according to some embodiments of the present disclosure.

FIG. 12 illustrates a comparison of the stability perovskite solar cells based on MAPbI₃ and MABr-treated MAPbI₃ films made by methods according to some embodiments of the present disclosure.

FIGS. 13A-F illustrate the effects of MABr concentration on smooth, pinhole-free MAPbI₃ thin films made by methods according to some embodiments of the present disclosure: Top view of SEM images of (FIG. 13A) a pinhole-free high-quality MAPbI₃ thin film and those treated with (FIG. 13B) 8 mg/mL, (FIG. 13C) 4 mg/mL, and (FIG. 13D) 2 mg/mL MABr solutions. Plots of (FIG. 13E) UV-vis absorption spectra and (FIG. 13F) XRD patterns of the high-quality MAPbI₃ thin films without and with MABr treatment at different concentrations, as indicated.

FIGS. 14A-C illustrate device characteristics based on high-quality pinhole-free MAPbI₃ thin films mad with and without MABr treatment, made by methods according to some embodiments of the present disclosure: (FIG. 14A) J-V curves, (FIG. 14B) EQE spectra, and (FIG. 14C) stabilized photocurrent density and power conversion efficiency biased near the maximum power point. 2 mg/mL MABr solution was used for the MABr treatment.

FIG. 15 illustrates J-V curves with both forward and reverse scans for cells made by methods according to some embodiments of the present disclosure: for the reverse scan, the device shows a PCE of 19.12%, with J_(sc) of 21.60 mA/cm², V_(oc) of 1.12 V, and FF of 0.793. For the forward scan, the device shows a PCE of 16.43%, with J_(sc) of 21.61 mA/cm², V_(oc) of 1.097 V, and FF of 0.693.

FIGS. 16A-D illustrate the effects of MAI treatment on XPS core-level analysis and film morphology for films made by methods according to some embodiments of the present disclosure: (FIG. 16A) XPS spectra of the Br 3d core-level region for MAPbI₃ thin films and those treated with low (2 mg/mL) and high (8 mg/mL) concentration MABr solutions. Top-view SEM images of (FIG. 16B) a high-quality MAPbI₃ thin film and those treated with 2 mg/mL (FIG. 16C) MABr and (FIG. 116D) MAI solutions.

FIG. 17 illustrates J-V curves with both forward and reverse scans for a cell made using MAI treatment according to some embodiments of the present disclosure: For the reverse scan, the device shows a PCE of 17.11%, with J_(sc) of 21.05 mA/cm², V_(oc) of 1.084 V, and FF of 0.749. For the forward scan, the device shows a PCE of 13.93%, with J_(sc) of 21.18 mA/cm², V_(oc) of 1.071 V, and FF of 0.614.

REFERENCE NUMBERS

-   100 perovskite -   110 cation -   120 cation -   200 method -   210 substrate -   215 raw materials -   220 depositing -   230 alkyl ammonium halide solution -   235 contacting -   245 heating -   250 volatiles -   255 multi-layered perovskite device -   310 alkyl ammonium metal halide film -   320 alkyl ammonium metal mixed-halide film -   325 perovskite intermediate device -   330 secondary alkyl ammonium metal mixed-halide film -   355 final perovskite device

DETAILED DESCRIPTION

Some embodiments of the present disclosure relate to contacting the surface of a perovskite material, e.g. an alkyl ammonium metal halide film such as a methyl ammonium lead iodide (MAPbI₃) film with a solution of a solvent (e.g. isopropanol (IPA) and/or tert-butanol) containing an alkyl ammonium halide, e.g. methyl ammonium bromide (MABr), methylammonium iodide (MAI), methylammonium chloride (MACl), and/or formamidinium chloride (FACl). The contacting may be followed by heating (e.g., between about 50° C. to about 300° C. or between about 100° C. to about 150° C.), such that the contacting and/or the heating result in the formation of an alkyl ammonium metal mixed-halide film (for example a mixed halide perovskite film such as MAPbI_(3-x)Br_(x), MAPbI_(3-x)Cl_(x), and/or MA_(1-y)FA_(y)PbI_(3-x)Cl_(x)), positioned on the alkyl ammonium metal halide film and/or at least partially infiltrating into the alkyl ammonium metal halide film, where x may be any value between greater than 0 and about 3. In some embodiments of the present disclosure, such a film of MAPbI_(3-x)Br_(x), or some other alkyl ammonium metal mixed-halide films, may extend from a few nanometers to a few hundred nanometers below the top surface of the alkyl ammonium metal halide film, or may extend from about one nanometer to about 1000 nanometers below the top surface of the alkyl ammonium metal halide film. In some embodiments of the present disclosure, an alkyl ammonium metal mixed-halide film may be positioned substantially on the alkyl ammonium metal halide film and have a thickness between about a few nanometers and about 1000 nanometers. For the example of bromine, the incorporation of bromine into the starting MAPbI₃ film (the starting alky ammonium metal halide film) and/or the creation of a separate MAPbI_(3-x)Br_(x) film (the resultant alkyl ammonium metal mixed-halide film) on the starting MAPbI₃ film as a result of the MABr contacting and/or heating is evidenced by several elecro-optical and structural characterizations (see below). It will be shown herein that the MABr-treated perovskite device has much improved stability at elevated temperature (˜100° C.) under light illumination. Moreover, it will be shown that device performance using MABr-treated perovskite films is much improved relative to the device performance of untreated MAPbI₃ films.

These findings support the concept that both solution (e.g. liquid) phase and/or vapor phase treatments of alkyl ammonium metal halide perovskite films, utilizing liquid- and/or vapor-phase alkyl ammonium halides may provide more stable and better performing perovskite devices. For example, a device having a first film of an alkyl ammonium metal halide may be contacted with an alkyl ammonium halide, where the alkyl ammonium metal halide has at least one halogen, and the alkyl ammonium halide has at least one halogen that is different from the halogen of the alkyl ammonium metal halide. The contacting may then result in the creation of a second film, an alkyl ammonium metal mixed-halide film, positioned on and/or incorporated into a top surface of the first film, where the second film includes at least one halogen from the first film and at least one halogen from the alkyl ammonium halide. Thus, the alkyl ammonium metal mixed-halide film may include two or more halogens, a mixed halide perovskite material, where the second film may be positioned on the first film and/or may be partially incorporated into a top surface of the first film.

Thus, the contacting may be achieved in some cases using solution methods. As used herein “film” and “layer” are interchangeable terms. In other examples, a bi-layer and/or multi-layer perovskite device may be achieved by a physical vapor deposition technique using different source materials. The resultant devices may have a relatively thin, bromine-rich outer film characterized by a wide band gap, such that the thin outer film may serve as a moisture-resistant film as well as an open-circuit voltage enhancer. In addition, the resultant device may have a thicker, bulk tri-iodide perovskite film/layer positioned below an outer film, which may possess excellent light absorber characteristics (e.g. narrow band gap). This gradient, bi-layer, and/or multi-layer structure may be implemented in a sandwiched and/or laminar structure (wide band gap films as top and bottom films), which may find applications in quantum wells for light-emitting diodes and other optoelectronic devices.

As described herein, an alkyl ammonium metal halide film and/or an alkyl ammonium metal mixed-halide film may be constructed from one more organo-metal halide perovskite materials. FIG. 1 illustrates that organo-metal halide perovskites may organize into cubic crystalline structures, as well as other crystalline structures such as tetragonal and orthorhombic, and may be described by the general formula ABX₃, where X (130) is an anion and A (110) and B (120) are cations, typically of different sizes (A typically larger than B). In a cubic unit cell, the B-cation 120 resides at the eight corners of a cube, while the A-cation 110 is located at the center of the cube and is surrounded by 6 X-anions 130 (located at the face centers) in an octahedral [MX₆]⁴⁻ cluster (unit structure). Typical inorganic perovskites include calcium titanium oxide (calcium titanate) minerals such as, for example, CaTiO₃ and SrTiO₃. In some embodiments of the present invention, the cation A (110) may include a nitrogen-containing organic compound such as an alkyl ammonium compound. Cation (120) may include a metal and anion B (120) may include a halide.

Additional examples for cation A (110) include organic cations and/or inorganic cations. Organic cations of A (110) may be an alkyl ammonium cation, for example a C₁₋₂₀ alkyl ammonium cation, a C₁₋₆ alkyl ammonium cation, a C₂₋₆ alkyl ammonium cation, a C₁₋₅ alkyl ammonium cation, a C₁₋₄ alkyl ammonium cation, a C₁₋₃ alkyl ammonium cation, a C₁₋₂ alkyl ammonium cation, and/or a C₁ alkyl ammonium cation. Further examples of organic cations of A (110) include methylammonium (CH₃NH³⁺), ethylammonium (CH₃CH₂NH³⁺), propylammonium (CH₃CH₂CH₂NH³⁺), butylammonium (CH₃CH₂CH₂CH₂NH³⁺), formamidinium (NH₂CH═NH²⁺), and/or any other suitable nitrogen-containing organic compound. In other examples, a cation A (110) may include an alkylamine. Thus, a cation A (110) may include an organic component with one or more amine groups. For example, cation A (110) may be an alkyl diamine halide such as formamidinium (CH(NH₂)₂).

Examples of metal cations 120 include, for example, lead, tin, germanium, and or any other 2+ valence state metal that can charge-balance the organo-metal halide perovskite 100. Examples for the anion X (130) include halides: e.g. fluorine, chlorine, bromine, iodine and/or astatine. In some cases, the organo-metal halide perovskite may include more than one anion X (130), for example pairs of halides; chlorine and iodine, bromine and iodine, and/or any other suitable pairing of halides. In other cases, the organo-metal halide perovskite 100 may include two or more halides of fluorine, chlorine, bromine, iodine, and/or astatine.

Thus, cation A (110), cation B (120), and anion X (130) may be selected within the general formula of ABX₃ to produce a wide variety of organo-metal halide perovskite 100, including, for example, methylammonium lead triiodide (CH₃NH₃PbI₃), and mixed halogen perovskites such as CH₃NH₃PbI_(3-x)Cl_(x) and CH₃NH₃PbI_(3-x)Br_(x). Thus, an organo-metal halide perovskite 100 may have more than one halogen element, where the various halogen elements are present in non-integer quantities; e.g. x is not equal to 1, 2, or 3. In addition, organo-metal halide perovskite, like other perovskites, can form three-dimensional (3-D), two-dimensional (2-D), one-dimensional (1-D) or zero-dimensional (0-D) networks, possessing the same unit structure.

As stated above, the anion A (110) may include an organic constituent in combination with a nitrogen constituent. In some cases, the organic constituent may be an alkyl group such as straight-chain or branched saturated hydrocarbon group having from 1 to 20 carbon atoms. In some embodiments, an alkyl group may have from 1 to 6 carbon atoms. Examples of alkyl groups include methyl (C₁), ethyl (C₂), n-propyl (C₃), isopropyl (C₃), n-butyl (C₄), tert-butyl (C₄), sec-butyl (C₄), iso-butyl (C₄), n-pentyl (C₅), 3-pentanyl (C₅), amyl (C₅), neopentyl (C₅), 3-methyl-2-butanyl (C₅), tertiary amyl (C₅), and n-hexyl (C₆). Additional examples of alkyl groups include n-heptyl (C₇), n-octyl (C₈) and the like.

FIG. 2 illustrates an example of a method 200 for producing a multi-layered perovskite device 255. The method 200 begins with depositing 220 an alkyl ammonium metal halide film onto a substrate 210. The depositing 220 of the alkyl ammonium metal halide film may be performed by one or more solution methods and/or by one or more vapor deposition methods that provide the required raw materials 215 (e.g. a metal halide, an alkyl ammonium halide, etc.). The alkyl ammonium metal halide film may be any alkyl ammonium metal halide such as a CH₃NH₃PbI₃ film. Thus, for the example of CH₃NH₃PbI₃, the alkyl is a methyl group, the metal is lead, and the halide is the halogen element iodine. In other examples, the metal may be lead, tin, and/or germanium. In other examples, the alkyl ammonium metal halide film may have an alkyl group that is a methyl group, a propyl group, and/or a butyl group. In other examples, the alkyl ammonium metal halide film may have a halogen that is iodine, bromine, and/or chlorine.

The deposited alkyl ammonium metal halide film may be modified by contacting 235 the alkyl ammonium metal halide film with an alkyl ammonium halide in a liquid solution 230. For example, the alkyl ammonium halide solution 230 may include an alkyl ammonium halide at least partially dissolved in a solvent. The alkyl ammonium halide in the solution may be a compound that contains a different halogen from the halogen present in the alkyl ammonium metal halide film formed by the depositing 220. The solvent used to formulate the alkyl ammonium halide solution 230 may be any solvent with a high solubility for the alkyl ammonium halide, while also having a low solubility for the alkyl ammonium metal halide film. The contacting 235 may modify a top portion of the alkyl ammonium metal halide film, such that an alkyl ammonium metal mixed-halide film forms within a top portion of the alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film includes a first halogen from the alkyl ammonium metal halide film, and a second halogen from the alkyl ammonium halide solution 230. Alternatively, the contacting 235 may deposit an alkyl ammonium metal mixed-halide film on top of the alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film may include the first halogen from the first alkyl ammonium metal halide film, and the second halogen from the alkyl ammonium halide solution 230. Alternatively, the contacting 235 may both modify a top portion of the alkyl ammonium metal halide film and deposit a thin alkyl ammonium metal mixed-halide film on top of the alkyl ammonium metal halide film. The modifying and depositing may together create a composite film of an alkyl ammonium metal mixed-halide film positioned on top of an alkyl ammonium metal halide film, where the alkyl ammonium metal mixed-halide film also penetrates into a portion of the top surface of the alkyl ammonium metal halide film, and where the composite film includes the first halogen from the alkyl ammonium metal halide film, and the second halogen from the alkyl ammonium halide solution 230. The contacting 235 may be by a solution method such as dip coating, spin coating, curtain coating, spraying, microgravure, and/or slot-die coating. Alternatively or in addition to, the contacting 235 may be accomplished by one or more vapor deposition methods.

The contacting 235 may be conducted at a temperature between about room temperature to about 200° C. The concentration of the alkyl ammonium halide solution 230 may be between about 3 mM and about 300 mM. The contacting 235 may be conducted in air or in an inert atmosphere for a duration between about 2 seconds and about 300 seconds. The contacting 235 may be conducted in air or in an inert atmosphere for a duration between about 2 seconds and about 30 seconds.

The first multi-layered perovskite device, as described above, may be further processed by heating 245. The heating 245 may remove volatiles 250, resulting in a second multi-layered perovskite device 255. In some embodiments, the contacting 235 and the heating 245 may be performed simultaneously. The heating 245 may allow for more complete formation/growth of the alkyl ammonium metal mixed-halide film on and/or within a top portion of the underlying alkyl ammonium metal halide film. In addition, the heating 245 may provide control over the thickness of the alkyl ammonium metal mixed-halide film. In some embodiments of the present disclosure, the first multi-layered perovskite device and/or the second multi-layered perovskite device 255 may have an alkyl ammonium metal halide film with a thickness between about 1 nm to about 1000 nm, and an alkyl ammonium metal mixed-halide film positioned with a thickness between about 1 nm to about 1000 nm, or in some embodiments between about 3 nm to about 300 nm, where the alkyl ammonium metal mixed-halide film is positioned on the alkyl ammonium metal halide film. The heating 245 may be conducted at or slightly above room temperature up to about 200° C., for a duration between about a few minutes (e.g., 5 minutes) and about several hours (e.g., 5 hours).

FIGS. 3A and 3B illustrate some embodiments of structures that may result from the methods described above. FIGS. 3A and 3B illustrate exemplary perovskite intermediate devices (325 a and 325 b) that may result from depositing (220 a and 220 b) alkyl ammonium metal halide films (310 a and 310 b) onto substrates (210 a and 210 b), as described above. Both perovskite intermediate devices (325 a and 325 b) include an alkyl ammonium metal halide film (310 a and 310 b) positioned on a top surface of the substrate (210 a and 210 b). However, the final multi-layered perovskite devices (355 a and 355 b) of FIGS. 3A and 3B resulting from the contacting (235 a and 235 b) and the optional heating (245 a and 245 b) described above for FIG. 2 may be different. In FIG. 3A, the final multi-layered perovskite device 355 a includes an alkyl ammonium metal mixed-halide film 320 a positioned on a top surface of an alkyl ammonium metal halide film 310 a. Thus, the alkyl ammonium metal halide film 310 a and the alkyl ammonium metal mixed-halide film 320 a may be substantially separate and distinct films that share an interface between them. In FIG. 3B, the final multi-layered perovskite device 355 b includes an alkyl ammonium metal mixed-halide film 320 b positioned above an alkyl ammonium metal halide 310 b. However, in addition, the final multi-layered perovskite device 355 b of FIG. 3B includes a secondary alkyl ammonium metal mixed-halide film 330 positioned between the alkyl ammonium metal halide film 310 and the alkyl ammonium metal mixed-halide film 320. Thus, FIG. 3B illustrates an example where the final multi-layered perovskite device 355 b results from a portion of a top thickness and the top surface of a first deposited alkyl ammonium metal halide film 310 being converted to the secondary alkyl ammonium metal mixed-halide film 330, with the additional formation of an alkyl ammonium metal mixed-halide film 320 on top of the newly converted secondary alkyl ammonium metal mixed-halide film 330.

In some embodiments of the present disclosure, an alkyl ammonium metal mixed-halide film 320 may result substantially entirely from the conversion of a top thickness and the top surface of the originally deposited alkyl ammonium metal halide film 310. Thus, most if not all of the alkyl ammonium metal mixed-halide film 320 may not result from the deposition of a new film on top of the originally deposited alkyl ammonium metal halide film 310. Instead, substantially all of the alkyl ammonium metal mixed-halide film 320 may originate from the originally deposited alkyl ammonium metal halide film 310. Without wishing to be bound by theory, there may be a strong driving force to mix at least a portion of an alkyl ammonium metal mixed-halide film 320 with at least a portion of an alkyl ammonium metal halide film 310; e.g. due to concentration gradients and/or thermal stimulus.

Examples

Experimental: Fluorine-doped tin oxide (FTO, TEC15, Hartford, Ind.) was patterned through a wet-etching method (H2 evolution reaction between zinc powder and hydrochloric acid), followed by an overnight base bath soaking (5 wt % NaOH in ethanol). A compact TiO₂ (c-TiO₂) layer was deposited by a spray pyrolysis of 0.2 M titanium diisopropoxide bis(acetylacetonate) in 1-butanol solution at 450° C. CH₃NH₃PbI₃ (or MAPbI₃) film was fabricated on top of c-TiO₂/FTO using a modified solvent engineering method. Precursor was made of 44 wt % of equimolar ratio of methyl ammonium iodide (MAI) and PbI₂ in γ-butyrolactone (GBL, Sigma-Aldrich)/dimethyl sulfoxide (DMSO, Sigma-Aldrich) (7/3 v/v). Substrate was span at 3500 rpm for 50 seconds, and a stream of toluene was injected during the spinning. The CH₃NH₃PbI₃ perovskite film (e.g. the alkyl ammonium metal halide film) was fully crystallized by annealing at 85° C. for 10 minutes. For MABr treatment (e.g. the alkyl ammonium halide solution), 160 ul MABr in 2-propanol solution (2 mg/ml) was dispersed on top of the first perovskite film during 4000 rpm spinning. A thermal annealing of 150° C. for 10 minutes was processed to remove the solvent and incorporate MABr into and/or onto the first perovskite film. Hole transport material (HTM) was deposited on top of perovskite film by 4000 rpm for 30 seconds using 2,2′,7,7′-tetrakis(N,N-dip-methoxyphenylamine)-9,9′-spirobifluorene (Spiro-OMeTAD, Merck) solution, which includes of 80 mg Spiro-OMeTAD, 30 μl bis(trifluoromethane) sulfonimide lithium salt (Li-TFSI) stock solution (500 mg Li-TFSI in 1 ml acetonitrile), 30 μl 4-tert-butylpyridine (TBP), and 1 ml chlorobenzene. Finally 150 nm Ag film was evaporated as a counter electrode using a shadow mask.

The J-V characteristics of the cells were obtained using a 2400 SourceMeter (Keithley) under simulated one-sun AM 1.5G illumination (100 mW cm⁻²) (Oriel Sol3A Class AAA Solar Simulator, Newport Corporation). A 0.12-cm² non-reflective mask was used to define the active area. External quantum efficiency was measured using a solar cell quantum efficiency measurement system (QEX10, PV Measurements). Stabilized power output was monitored by a potentiostat (VersaSTAT MC, Princeton Applied Research) near a maximum power output point. X-ray diffraction of the perovskite thin films was performed using a X-ray diffractometer (Rigaku D/Max 2200) with Cu Kα radiation. Absorption spectra were carried out by a ultraviolet-visible (UV/vis) spectrometer (Cary-6000i).

X-ray photoemission spectroscopy measurements were performed on a Kratos NOVA spectrometer calibrated to the Fermi edge and core-level positions of sputter-cleaned metal (Au, Ag, Cu, Mo) surfaces. XPS spectra were taken using monochromated Al Kα radiation (1486.7 eV) at a resolution of 400 meV and fit using Pseudo-Voigt profiles.

Results: FIGS. 4A and 4B illustrate scanning electron microscopy (SEM) images of the top view of the (FIG. 4A) first deposited MAPbI₃ film and (FIG. 4B) the MABr treated MAPbI₃ film. The grain size for the first deposited MAPbI₃ film is generally smaller than 500 nm, and a noticable amount of pinholes can be observed. The MABr treatment not only eliminates those pinholes, it also increases the apparent grain size to 1-2 micrometer level.

FIG. 5 illustrates ultraviolet-visible (UV-vis) absorption spectra of first deposited MAPbI₃ films with and without the MABr treatment. The MABr treatment blue shifts the absorption edge by about 10 nm. This slight spectral shift indicates the low-degree of incorporation of Br into the MAPbI₃. This implies that the MABr-treated MAPbI₃ sample contains MAPbI_(3-x)Br_(x) (e.g. the alkyl ammonium metal mixed-halide). For reference, MAPbI₂Br is expected to blue shift the absorption spectrum by about 100 nm relative to that of the standard MAPbI₃ sample. It is worth noting that the MABr-treated sample has essentially the same absorbance intensity as the one without MABr treatment.

FIG. 6 illustrates X-ray diffraction patterns of the first deposited MAPbI₃ films with and without MABr treatment. The main characteristic perovskite peak around 14 degree increases by about a factor of five after the MABr treatment, indicating enhanced crystallinity. This observation is consistent with the larger average grain size for the MABr-treated film shown in FIGS. 4A and 4B. It is noted that the MAPbI₃ film treated with the MABr solution film exhibits a longer photoluminescence decay time (see FIGS. 7A and 7B) than the starting MAPbI₃ film sample, indicating a passivation effect with the MABr treatment that could be associated with the overall improvments in the MAPbI_(3-x)Br_(x) film quality.

FIG. 8 illustrates x-ray photoelectron spectroscopy (XPS) measurements of core level analysis of MAPbI₃ with and without MABr treatment. In addition to the strong I 3d signal for all samples, there is a clear Br 3d signal for the MABr treated films, especially for the film treated with a higher MABr concentration (˜10 mg/ml). The lower concentration (˜2 mg/ml), which is used for other measurement, also has a clear but much weaker Br 3d signal.

FIG. 9 illustrates shows the typical photocurrent density-voltage (J-V) curves of the MAPbI₃- and MAPbI_(3-x)Br_(x)-based solar cells. It is noteworthy that for these devices the initial MAPbI₃ films have mediocre (relatively poor) film quality as shown in FIGS. 4A and 4B. However, a substantial performance improvement was obtained by treating the initial MAPbI₃ with a MABr solution. The MAPbI₃-based PSC shows about 14.65% power conversion efficiency (PCE) with a short-circuit photocurrent density (J_(sc)) of 19.93 mA/cm², open-circuit voltage (V_(oc)) of 1.042 V, and fill factor (FF) of 0.705. With the 2 mg/mL MABr treatment, the device performance for MAPbI_(3-x)Br_(x)-based PSC increases to 17.38% with a J_(sc) of 20.68 mA/cm², V_(oc) of 1.092 V, and FF of 0.770. The improved device performance with all photovoltaic parameters is consistent with the improved structural and electro-optical properties (e.g., higher crystallinity, larger grain size, and fewer surface defects) of MAPbI_(3-x)Br_(x) films in comparison to the pristine MAPbI₃ films.

FIG. 10 illustrates external quantum efficiency (EQE) spectra of solar cells based on MAPbI₃ films and MAPbI₃ films that were MABr-treated. The spectral shift near the EQE onset around 800 nm is consistent with the observed blue shift in the absorption spectra in FIG. 5. The MABr-treated sample shows higher efficiency values across a wide spectral range despite their similar absorbance values in this spectral range. This indicates that the MABr treatment also improves charge-separation and/or charge-collection processes. Thus, besides the higher PV performance in efficiency, the MAPbI_(3-x)Br_(x) films resulting from treating the starting MAPbI₃ films with a MABr solution also exhibit enhanced stability.

FIGS. 11A-D illustrate photos of an as-prepared (FIG. 11A) MAPbI₃ film and (FIG. 11B) a MABr-treated MAPbI₃ film. Photos of (FIG. 11C) MAPbI₃ film and (FIG. 11D) MABr-treated MAPbI₃ film after annealing at 95° on a hotplate in humid air (60% relative humidity) for 15 hours. The yellowing shown in (FIG. 11D) is clear indication of decomposition of the MAPbI₃ film. In contrast, the MABr-treated film in (FIG. 11C) shows much improved thermal stability in humidity air.

FIG. 12 illustrates a comparison of the stability perovskite solar cells based on MAPbI₃ and MABr-treated MAPbI₃ films. About 4-12 individual cells were measured for each type of devices to check the statistics of device performance. The MAPbI_(3-x)Br_(x) perovskite solar cell resulting from treating the starting MAPbI₃ films with a MABr solution is much more stable than the starting MAPbI₃ films. This stability improvement may be attributed to Br inclusion into the final device, and also due to the larger crystal grain sizes.

MABr Concentration Effect.

To further explore the importance of the MABr solution and its concentration for this observed film and device improvement the effect of varying MABr solution concentration on the properties of the final treated MAPbI_(3-x)Br_(x) films was studied. The average or low-quality MAPbI₃ films prepared with standard solvent techniques can vary significantly from batch-to-batch and/or within different areas of the same sample. Therefore, for the studies described in this section, the high-quality MAPbI₃ films were cut from a large-area sample to insure good quality and reliable material properties. FIGS. 13A-D illustrate SEM images of a high-quality MAPbI₃ film and those of high-quality MAPbI₃ films treated with different MABr concentrations (from 2 to 8 mg/mL). The high-quality MAPbI₃ film is compact and pinhole-free with crystal sizes ranging from 200-500 nm. With an 8 mg/mL MABr treatment, the crystal size of MAPbI_(3-x)Br_(x) becomes larger than the MAPbI₃ film, but there is clear evidence of pinhole formation and the surface also becomes rougher, which is similar to the films prepared with the spin-coating-based sequential deposition method. When the MABr concentration is reduced to 4 mg/mL, the MAPbI_(3-x)Br_(x) film becomes less coarse with larger crystal size than the MAPbI_(3-x)Br_(x) film treated with 8 mg/mL MABr solution. With further reduction of the MABr concentration to 2 mg/mL, the MAPbI_(3-x)Br_(x) film becomes compact with micron-sized (up to 1-2 μm) grains containing some small perovskite nanocrystals. Such dramatic morphology change is similar to those obtained from a low-quality MAPbI₃ film (see FIGS. 4A and 4B), suggesting that this simple post-growth treatment with a low-concentration MABr solution may effectively reconstruct perovskite thin films such that the initial structural defects from a low-quality perovskite thin film may be significantly improved.

With increasing MABr concentration, the UV-vis absorption data (see FIG. 13E) show a systematic blue shift of the absorption edge for the MABr-treated MAPbI_(3-x)Br_(x), suggesting a higher amount of Br incorporation. When the high-quality MAPbI₃ film is treated with an 8 mg/mL MABr solution, the UV-vis absorption spectrum of the resulting film exhibits an ˜12-nm blue shift of the absorption edge but no obvious change in the absorbance. The shift in the absorption edge with increasing MABr concentration is a clear indication of Br inclusion into MAPbI₃ to form the mixed-halide MAPbI_(3-x)Br_(x), which is consistent with the XRD results. The (110) peak location increases very slightly but noticeably from about 14.10 to 14.14 degrees with 8 mg/mL MABr treatment. However, the peak intensity reaches a maximum at 2 mg/mL MABr followed by a continuous decrease with higher MABr concentration, which may be caused by the deterioration of the grain morphology (as shown in FIGS. 13A-D).

Although the compositional change of the MAPbI₃ film caused by the mild 2 mg/mL MABr treatment is very minimum as reflected by the small absorption edge shift (<5 nm) and almost identifical XRD peak positions (shifted by ˜0.01°-0.02°), the morphology change and XRD peak intensity increase are very dramatic, and more importantly, such changes have very little dependence on initial MAPbI₃ film quality (see FIG. 13F). The very small compositional change is consistent with the X-ray photoelectron spectroscopy (XPS) measurement (FIG. 16A), which suggests a small amount (˜1%) of Br incorporation in the surface layer of 2 mg/mL MABr-treated perovskite film. FIG. 14A shows the J-V curves for PSCs based on the high-quality MAPbI₃ films with and without the 2 mg/mL MABr treatment. The pristine MAPbI₃-based PSC displays a best PCE of 16.63% with J_(sc) of 20.67 mA/cm², V_(oc) of 1.08 V, and FF of 0.746. Such a performance level is also consistent with previous reports using the standard solvent-engineering or fast-crystallization processing. With the MABr treatment, the device efficiency reaches 19.12% with J_(sc) of 21.60 mA/cm², V_(oc) of 1.12 V, and FF of 0.793. The improvement of device parameters is very similar to the devices based on average/low-quality perovskite film. FIG. 14B compares the EQE spectra of the two devices shown in FIG. 14A. The integrated current densities match well with their corresponding J_(sc) values from the J-V curves. Because there is still a noticable (and expected) hysteresis behavior for this compact-TiO₂-based planar PSC (FIG. 15), a stabilized power output was measured over time near the maximum power output point to verify the performance of the PSC. FIG. 14C shows that a 18.3% PCE was steadily recorded over several minutes, which matches the J-V curve reasonably well and further attests the effectiveness of the simple MABr treatment to improving device performance.

In contrast to the much-improved device performance with 2 mg/mL MABr treatment, the PSCs based on 8 and 4 mg/mL treated MAPbI_(3-x)Br_(x) films exhibit lower device performance, especially the one with 8 mg/mL MABr treatment (see Table 1 below). This concentration dependence is consistent with the structure/morphology changes discussed in connection with FIGS. 13A-F along with the change in stoichiometry. These results suggest that the simple Br incorporation may not significantly increase PSC performance by only forming MAPbI_(3-x)Br_(x) perovskite films with relatively high Br concentration without affecting the perovskite film/structure properties.

TABLE 1 MABr concentration effect on the typical photovoltaic parameters. Standard deviations from 8-12 cells for each type of devices are given. For these devices, high-quality MAPbI₃ films (FIG. 3A) were used as the initial films prior to MABr treatment. MABr Concentration J_(sc) V_(oc) PCE (mg/mL) (mA/cm²) (V) FF (%) 0 20.54 ± 0.07 1.052 ± 0.027 0.724 ± 0.012 15.64 ± 0.63 2 21.86 ± 0.12 1.120 ± 0.010 0.754 ± 0.020 18.50 ± 0.39 4 21.48 ± 0.28 1.056 ± 0.005 0.734 ± 0.014 16.66 ± 0.48 8 21.27 ± 0.16 1.049 ± 0.011 0.665 ± 0.031 14.83 ± 0.47

FIG. 16A shows XPS measurements of the MAPbI₃ films after 2 mg/mL and 8 mg/mL MABr treatment. In addition to the strong I 3d signal for all samples (see FIGS. 7A and 7B), there is a clear but weak Br 3d signal for the 2 mg/mL MABr-treated films. XPS measurements indicate a very low concentration of <1% for bromine in the halide content in the surface layer. Such low Br concentration is consistent with the XRD results and UV-vis spectra of the MABr-treated MAPbI_(3-x)Br_(x) film (see FIGS. 13E and 13F). In contrast, the 8 mg/mL MABr-treated MAPbI_(3-x)Br_(x) has almost 8 times higher Br concentration than the 2 mg/mL MABr-treated sample.

The abovementioned results clearly demonstrate that the MABr treatment methods described herein, when utilizing the proper concentrations, are effective at converting an average or sub-average MAPbI₃ perovskite film into a high-quality MAPbI_(3-x)Br_(x) film with larger crystal size and higher crystalline order. It appears that the MABr solution with low concentration such as 2 mg/mL may induce the recrystallization of the small-sized MAPbI₃ into perovskite films with much larger final grain sizes. In contrast, the higher-concentration MABr treatments may only induce a Br/I halide exchange reaction in the MAPbI₃ film without significantly affecting the grain growth. The most interesting finding from this two-step perovskite crystal growth process is that it is largely invariant to the initial MAPbI₃ film quality (see FIGS. 4A, 4B, 5, and 6 and FIGS. 13A-F).

Thus, a process for fabricating high-quality MAPbI_(3-x)Br_(x) may be divided into two steps. The first step may include the formation of MAPbI₃ precursor nanocrystals by standard solvent and/or vapor-phase deposition methods to form a relatively compact thin film. The second step may then include conversion of the first-formed MAPbI₃ precursor nanocrystals into higher quality MAPbI_(3-x)Br_(x) perovskite films with larger crystal sizes by contacting the first-formed MAPbI₃ precursor nanocrystals with a MABr-containing solution. Thus, such a two-step process, with a second MABr treatment step, may convert both high quality and low quality MAPbI₃ perovskite films into final MAPbI_(3-x)Br_(x) thin films with high quality. However, the process is MABr concentration dependent. For high-concentration (e.g., 8 mg/mL) MABr solutions, the dissolution of small-size MAPbI₃ may be inhibited by the intercalation of MABr or the I/Br cation exchange reaction, which could account for less morphology change or grain-size growth found with the high-concentration MABr treatment. For low-concentration (e.g., 2 mg/mL) MABr treatments, the small-sized MAPbI₃ crystals may be quickly dissolved and regrown into larger crystals.

To further test whether the observed perovskite reconstruction is not simply resulting from excess organic salt, the effect of using a similar MAI treatment on the morphology changes of MAPbI₃ film was studied. FIG. 16D shows the SEM image of a high-quality MAPbI₃ film after post-growth treatment with 2 mg/mL MAI solution. For comparison, the SEM images of the pristine MAPbI₃ film and the MABr-treated MAPbI_(3-x)Br_(x) film are shown in FIGS. 16B and 16C, respectively. The grain size increased slightly with MAI treatment; however, the degree of grain growth was significantly limited in comparison to the MABr treatment. The best PSC based on MAI treatment shows a PCE of about 17.11% (see FIG. 17), which is significantly lower than the performance of a PSC based on the MABr treatment. These results suggest that besides the MABr concentration, using MABr itself (rather than MAI) may also be important to the process.

As used herein, the term “substantially” refers to the inherent variability present in attempts to attain an exact design parameter. For example, when describing solubility as “substantially soluble” or “substantially insoluble” it is clear of to one of ordinary skill in the art that there for “substantially soluble” Component A, there may still be small concentrations of insoluble Component A in the solution. Similarly, for “substantially insoluble” Component B, there may be small concentrations of soluble Component B in the solution. Similarly, “substantially” separate and distinct films that share an interface indicate that the films may be essentially layered and/or laminated with a distinct interface between them. However, the films may also have less areas at the interface that are less defined, due at least to a portion of one layer being transformed into part of the second layer. Thus, the interface between a first layer and a second layer may include a third transition layer between the first layer and the second layer.

The foregoing discussion and examples have been presented for purposes of illustration and description. The foregoing is not intended to limit the aspects, embodiments, or configurations to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the aspects, embodiments, or configurations are grouped together in one or more embodiments, configurations, or aspects for the purpose of streamlining the disclosure. The features of the aspects, embodiments, or configurations, may be combined in alternate aspects, embodiments, or configurations other than those discussed above. This method of disclosure is not to be interpreted as reflecting an intention that the aspects, embodiments, or configurations require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive aspects lie in less than all features of a single foregoing disclosed embodiment, configuration, or aspect. While certain aspects of conventional technology have been discussed to facilitate disclosure of some embodiments of the present invention, the Applicants in no way disclaim these technical aspects, and it is contemplated that the claimed invention may encompass one or more of the conventional technical aspects discussed herein. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate aspect, embodiment, or configuration. 

1-17. (canceled)
 18. A device comprising, in order: an alkyl ammonium metal halide film comprising a first halogen; and an alkyl ammonium metal mixed-halide film comprising the first halogen and a second halogen, wherein: the alkyl ammonium metal halide film has a thickness of about 1 nanometer to about 1000 nanometers, and a thickness of the alkyl ammonium metal mixed-halide film is less than or equal to the thickness of the alkyl ammonium metal halide film.
 19. The device of claim 18, wherein the thickness of the alkyl ammonium metal mixed-halide film is between about 1 nanometers to about 1000 nanometers.
 20. The device of claim 18, wherein the metal comprises at least one of lead, tin, or germanium.
 21. The device of claim 18, wherein the alkyl ammonium metal halide film comprises at least one of CH₃NH₃PbI₃ or CH(NH₂)₂PbI₃.
 22. The device of claim 18, wherein: the alkyl ammonium lead mixed-halide film comprises at least one of CH₃NH₃PbI_(3-x)Br_(x) or CH(NH₂)₂PbI_(3-x)Br_(x), and x is between greater than 0 and about
 3. 23. The device of claim 18, wherein the thickness of the alkyl ammonium metal halide film is between about 3 nanometers and about 300 nanometers.
 24. The device of claim 18, wherein the alkyl ammonium metal mixed-halide film further comprises a grain having a characteristic length between about 1 micron and about 2 microns.
 25. The device of claim 18, wherein the alkyl ammonium metal mixed-halide film further comprises a (110) peak location at 14.14 degrees, as measured by XRD. 